Jointing / Gasket Material

KLINGER C-4400 - NON-Metallic Sheets & Gaskets

Price: Contact

  • Model: KLINGER C-4400
  • KLINGER C-4400 - NON-Metallic Sheets & Gaskets

    KLINGER C-4400

     

    KLINGER C-4400

    Typical Values
    Compressibility(ASTM F 36 J)   % 11
    Recovery(ASTM F 36 J) min % 55
    Stress relaxation (DIN 52913) 50Mpa, 16h/175℃ Mpa 28
    50Mpa, 16h/300℃ Mpa 25
    Stress relaxation (BS 7531) 40Mpa, 16h/300℃ Mpa 23
    Klinger cold/hot compression 50 Mpa thickness decrease at 23℃ % 10
    thickness decrease at 300℃ % 20
    Tightness according DIN 3535/6   mg/s x m 0.02
    Tightness class L DIN 28090-1   0.1
    Specific leakrate λ VDI 2440 mbar x l/s x m 16.4E-08
    Cold compression DIN 28091-2 % 8 - 12
    Cold recovery DIN 28091-2 % 3 - 5
    Hot compression DIN 28091-2 % < 15
    Hot recovery DIN 28091-2 % 1
    Spring back R DIN 28091-2 mm 0.019
    Thickness increase after fluid immersion(ASTM F 146) Oil JRM 903:5h/150℃ % 3
    Fuel B:5h/23℃ % 5
    Density   g/cm3 1.6
    Average surface resistance ROA Ω 3.6×10E10
    Average specific volume resistance PD Ω cm 1.4×10E10
    Average dielectric strength   kV/mm 24
    Average power factor 1kHz, ca, 3mm thickness tanδ 0.147
    Average dielectric coefficient   εr 9.7
    Thermal conductivity 1kHz, ca, 3mm thickness    
    ASME-Code sealing factors W/mK 0.40-0.42
    for gasket thickness 2.0mm tightness class 0.1mg/ s x m MPa y 20
    m 3.5

    Related projects

    Category
    Online support
  • Consulting - Quotation
    Consulting - Quotation
  • Consulting-Technical
    Consulting-Technical
  • Consulting - Quotation
    Consulting - Quotation
  • Consulting - Technical
    Consulting - Technical
  • Consulting - Quotation
    Consulting - Quotation