WOOJU Gasket

Graphite Sheet & Gasket Wj 8000/ Wj 8000-P/ Wj 8000-B/ Wj 8000-W/ Wj 7000-B

Price: Contact

  • Model: Wj 8000/ Wj 8000-P/ Wj 8000-B/ Wj 8000-W/ Wj 7000-B
  • Graphite Sheet & Gasket

    Model: Wj 8000/ Wj 8000-P/ Wj 8000-B/ Wj 8000-W/ Wj 7000-B

    Graphite Sheet & Gasket

     

    Wj 8000

    Pure Graphit Film

    Wj 8000-P

    Stainless steel Flat
    Reinforced Graphite Sheet

    Wj 8000-B

    Stainless steel Tanged
    Reinforced Graphite Sheet

    Wj 8000-W

    Stainless steel Wire-Mesh
    Reinforced Graphite Sheet

    Wj 7000-B

    Stainless steel Mica Sheet
    (It can be used up to 900 ℃ by reinforcing mica in stainless steel.)

    Characteristic

    Graphite sheet gasket have good adhesion with flange. These are good to sealing performance even in the lower whole surface stress, and no material change depending on temperature change. So, it is widely used in ultimate low to high temperature also excellent to non scaling property and chemical resistance. In order to improve use of problem in pure graphite sheet, it is applied to reinforced sheet by stainless steel(plate ,tang, wire)

    Maxium Working Conditions

    Temperature during
    continuous opertion
    450
    Temperature during continuous
    opertion in steam
    550
    Pressure MPa 12

    Dimensions

    Standard Thickness of a Sheet mm 1.0, 1.5, 2.0, 3.0 ±10%
    Standard Size of a Sheet mm 1,000 × 1,000
    1,500 × 1,500
    ±20.0

    Physical and Chemical Properties

    Graphite Density (±5%) g/cm3 1.0 Din 28090-2
    Tensile Strength (Min.) MPa 20 ASTM F152
    Compressibility % 35-45 ASTM F36
    Residual Stress 16h/300℃ (Min.) % 15-20 ASTM F36
    Residual Stress 16h/300℃ (Min.) MPa 38 BS 7531
    Residual Stress 16h/300℃ (Min.) MPa 48 Din 52913
    Ash Content (Max.) % 0.5 Din 51913

    Related projects

    Category
    Online support
  • Consulting - Quotation
    Consulting - Quotation
  • Consulting-Technical
    Consulting-Technical
  • Consulting - Quotation
    Consulting - Quotation
  • Consulting - Technical
    Consulting - Technical
  • Consulting - Quotation
    Consulting - Quotation